The organic binder was selected by detection of plasticity and drying property of the body. 通过坯料可塑性和干燥性能的测定,对有机粘结剂进行了筛选。
Improving strength of iron ore pellet containing organic binder by microwave heating 微波加热提高有机粘结剂铁矿球团的强度
Following burnout of the organic binder, the boards are white in color. 有机粘合剂燃尽后,板材的颜色为白色。
Effect of Organic Binder in Screen-printing TiO_2 Paste on Dye-sensitized Solar Cells 染料敏化太阳能电池丝网印刷浆料中有机造孔剂对电池性能的影响
The experimental results show that the coating has higher strength contained PVA organic binder than con-tained colloidal silica inorganic binder at room temperature. 结果表明,采用PVA有机粘结剂的涂料常温强度高于硅溶胶无机粘结剂涂料的常温强度。
The magnesia based big brick was produced by using quality fused magnesite with high calcia and low silica, composite additives and composite organic binder. 采用优质电熔高钙低硅镁砂,添加复合外加剂,用复合有机结合剂结合,制成了镁质大砖。
Study on a Water soluble Organic Binder Sand Cured by Microwave Energy 微波固化水溶性有机粘结剂砂的研究
Gypsum-based building putty has changed the traditional technology mode, in which the solid component is used only as inert filler, and the stiffening of putty depends completely on film forming of the organic binder. 石膏基建筑腻子改变了传统建筑腻子中固体组分仅作为惰性填料,腻子硬化完全依赖有机粘结剂固化成膜的技术模式。
Evaluation of DRI Produced with Organic Binder Pellets 对采用有机粘结剂球团生产DRI产品的评价
Lowering bentonite level in pellets by adding organic binder 使用有机粘结剂降低球团矿中膨润土用量的研究
The results show that the application of intensive mixer for preparation of mixture with addition of the organic binder is feasible and the quality of both green pellets and dry pellets can meet the requirement of DR process. 结果表明:采用强力混合机进行添加复合有机粘结剂的混合料制备,在工艺技术上是可行的,其生球、干球质量均可满足直接还原工艺的要求。
This paper analyses the effect of inorganic, organic binder and inorganic/ organic compound binder on pelletizing properties, meanwhile discusses the relation between the ratio and size of binders and pelletizing quality index. The respective merits and defects are presented. 分析了无机、有机及无机/有机复合粘结剂对球团性能的影响,同时讨论了粘结剂粒度和配量与球团性能指标的关系,并指出了各类粘结剂的优缺点。
Variation of sinter FeO content after addition of HPL organic binder in sinter mix 添加HPL有机粘结剂后烧结矿FeO含量的变化
In this paper, the molecular structure mould ( X P K) of organic binder is proposed. 为此,提出了理想的有机粘结剂分子构型(XPK)。
The influence of the ceramic powder and the formulation of the organic binder ( especially the surfactant) on the ceramic feedstock, and the green and sintered parts are discussed in detail. 详细论述了陶瓷粉体性质、有机载体组成特别是表面活性剂对于陶瓷喂料和注射成型所成坯体性质的影响。
The organic binder extraction of injection moulded body is key step in this fabricating technology. 在这一陶瓷制备技术中,注射成型体的脱脂过程是关键一环。
Before the marked self-reduction of the pellets at 1 000 ℃, the high temperature strength depends on organic binder; 在球团开始显著的自还原反应之前,球团高温强度主要由有机黏结剂来保证;
This paper presents the results from the second experiment which have shown that after adding organic binder, the green pellet strength exceeds 29. 4N/ P and that of the dried pellets exceeds 88. ZN/ p both for conventional pellets and composite pellets. 试验结果表明,添加有机粘结剂后,普通球团和复合球团湿球抗压强度都在29.4N/个以上,干球在88.2N/个以上。
The influences of organic binder G on granulation are studied. With the addition of binder G the wetting angle of water on fine ore surface is decreased, which results in the hydrophilicity enhancement of the fine ore and strengthens the granulation process. 研究了添加有机粘结剂G对制粒过程的影响.结果表明,添加有机粘结剂G使水在矿粉颗粒表面的润湿角降低,提高了矿粉的亲水性,强化了制粒过程;
Organic binder was used for making carbon-bearing briquette with manganese ore and coke fines in the experiment. 用有机粘结剂和焦粉制备配碳锰矿团块。
Study and choice of organic binder for iron ore pellets containing carbon 竖炉型含碳球团有机粘结剂的选择与应用
Coupling agents have important effects in the aspect of increasing the compatibility between ceramic powder and organic binder, and can induce viscosity and improve ceramic solid content of the slurry. 偶联剂能够增加陶瓷粉体和有机载体的相容性,起到降低浆料体系粘度和增加陶瓷固相体积分数的作用。
Especially in recent years, with the organic binder of the widely used, so that a large number of resin core sand mixed in the used clay sand, and take shape the clay ( mixed) used sand. 尤其是近年来,随着有机粘接剂的广泛应用,使粘土旧砂中混入了大量的树脂芯砂,形成粘土(混合)旧砂。
This illuminated that organic binder was good material to develop new type non-envelope control release fertilizer, and nutrient controlled release was achieved by the way of granulation at one time. 这说明有机粘结剂可以作为开发新型非包膜型控释肥的良好材料,通过造粒可以同时实现对养分的控制释放。
The results demonstrate that the interaction modes of two heat sources are totally different from each others for different cladding methods, i.e. pre-placed coating by thermal spraying, pre-placed coating by organic binder and powder feeding in laser-induction hybrid cladding. 研究结果表明,对于氧乙炔热喷涂层、冷预涂层和自动送粉式激光&感应复合熔覆,激光和感应两种热源的作用方式是不同的。
The result of leaching examination showed that organic binder was better in favor of delaying nutrient release than inorganic binder. 淋溶试验结果表明有机粘结剂比无机粘结剂有利于延缓颗粒肥速溶养分的释放。
Bond forming tests including organic binder, calcium, inorganic adhesive series pilot; preparation of composite adhesive for bonding test; use coking coal and organic binder mixed with coke test. 粘接成型试验包括对有机粘接剂、钙系列的无机粘接剂进行试验;配制复合粘接剂进行粘接试验;选用主焦煤与有机粘接剂混合用型焦试验。
Comparison between organic binder and inorganic binder, organic binder was able to delay nutrient release of N, P and K in granular organic compound fertilizer obviously, especially the effect of delaying P release was most obvious. 与无机粘结剂相比,有机粘结剂可明显降低有机复混肥中氮、磷和钾的释放速度,尤其对磷素效果最为明显。
Blending a small amount of bituminous coal and anthracite in the organic binder by kneading, molding, carbonization temperature indicators available to meet the coke product. 将少量烟煤配入无烟煤中与有机粘接剂经混捏、成型、高温炭化后可得到符合指标的型焦产品。